310S / 1.4951 Stainless Steel Coil

310S / 1.4951 Stainless Steel Coil 310S (old grade 0Cr25Ni20/ new grade 06Cr25Ni20) is an austenitic chromium-nickel stainless steel with good oxidation resistance and corrosion resistance, due to the higher percentage of chromium and nickel, 310S has much better creep strength, can continue to work at high temperatures, has good high temperature resistance. 310S stainless steel is austenitic chromium-nickel stainless steel, has good oxidation resistance, corrosion resistance, high temperature resistance, because of the higher percentage of chromium and nickel, making it has much better creep strength, can continue to work at high temperature, has good high temperature resistance. Because of the high content of nickel (Ni), chromium (Cr), has good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature…

  • Product Details

310S / 1.4951 Stainless Steel Coil

310S (old grade 0Cr25Ni20/ new grade 06Cr25Ni20) is an austenitic chromium-nickel stainless steel with good oxidation resistance and corrosion resistance, due to the higher percentage of chromium and nickel, 310S has much better creep strength, can continue to work at high temperatures, has good high temperature resistance.

310S stainless steel is austenitic chromium-nickel stainless steel, has good oxidation resistance, corrosion resistance, high temperature resistance, because of the higher percentage of chromium and nickel, making it has much better creep strength, can continue to work at high temperature, has good high temperature resistance.
Because of the high content of nickel (Ni), chromium (Cr), has good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance, high temperature resistant steel pipe is dedicated to the manufacture of electric furnace tube and other occasions, austenitic stainless steel increases the content of carbon, due to its solid solution strengthening effect so that the strength is improved,

The austenitic stainless steel has high strength and creep strength at high temperature due to its face-centered cubic structure, which is based on chromium and nickel.
Melting point 1470℃, 800℃ began to soften, allowable stress continued to reduce.Improve the common carbon tool steels brittle nature, and to extend the life of tools.
Vacuum degassing refining steel, stable quality.
Good hardenability, oil cold hardening (quenching and deformation less) good toughness and wear resistance, durable tools.

Equivalent Material of 310S Stainless Steel Coil

Grade Euronorm China GB Japanese JIS
No.
310S 1.4951 06Cr25Ni20 SUS310S

Standard Specification Of 310S Coil

Thickness 0.3mm-12.0mm
Width 600mm, 700mm, 800mm, 900mm, 1000mm, 1200mm, 1220mm, 1500mm, etc
Length Per Coil
Surface 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc
Finish Cold rolled coil (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats,
Blank (Circle), Ring (Flange) etc.

310S stainless steel composition content.

Grade C Mn Si P S Cr Mo Ni N
310S Min.
Max.
≤0.08 ≤2.0 ≤1.5 ≤0.035 ≤0.03 24.00-26.00 / 19.00-22.00

Ob (MPa) 520 or higher, o0.2 (MPa) 205 or higher, the delta 5 (%) of 40 or higher, Ψ (%) of 50 or more, HB 187 or less can withstand temperatures up to 1150 ℃.
Melting point at 1398 ℃ ~ 1454 ℃
Tempering: 180 ~ 200
Annealing condition, ≤207HB, indentation diameter ≥4.20mm
Quenching, p 62 HRC